From comments I've seen, as-cast aluminum is soft and "gummy". Even if strength weren't an issue operationally, soft gummy aluminum is a pain in the wazoo to machine -- any manufacturer is going to want to heat treat it just to make it machine nicely.
Dunno about the alloy -- what makes you think 713 would be better?